40Cr钢材介绍
40Cr钢材是机械制造业使用最广泛的钢之一。调质处理后具有良好的综合力学性能,良好的低温冲击韧性和低的缺口敏感性。钢的淬透性良好,水淬时可淬透到Ф28~60mm,油淬时可淬透到Ф15~40mm。这种钢除调质处理外还适于氰化和高频淬火处理。切削性能较好,当硬度为HB174~229时,相对切削加工性为60%。该钢适于制作中型塑料模具。
40Cr钢的化学成分(GB/T3077-1999)ω/%
C | Si | Mn | Cr | S | P | Ni | Cu |
0.37~0.45 | 0.17~0.37 | 0.50~0.80 | 0.80~1.10 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.030 |
物理性能
40Cr钢的化学成分示于表4-8-2~4-8-5,其密度为7.82t/m3。
表4-8-2 40Cr钢的临界温度
临界点 | Ac1 | Ac3 | Ms | 备注 |
温度(近似值)/℃ | 780 770 | 840 805 | 350 328 | 1 2 |
1 用钢成分(%):0.38C,0.30Si,0.66Mn,0.95Cr,0.18Ni,0.016P,0.028S;
2 用钢成分(%):0.42C,0.29Si,0.69Mn,0.87Cr,0.14Ni,0.010P,0.013S。
表4-8-3 40Cr钢的弹性模量和切变模量
弹性模量E(20℃) | /MPa | 200000~211700 |
切变模量G(20℃) | 80800 |
表4-8-4 40Cr钢的线(膨)胀系数
温度/℃ | 20~200 | 20~300 | 20~400 | 20~500 | 20~600 | 20~700 | 备注 |
线(膨)胀系数/C-1 | (11.9~12.0) ×10-6 | (13.3~13.4)×10-6 | (14.3~14.4)×10-6 | (15.0~15.1)×10-6 | (15.3~15.4)×10-6 | (15.4~15.5)×10-6 | 1 2 |
1 用钢成分(%):0.37C,0.30Si,0.66Mn,0.95Cr,0.18Ni,0.016P,0.028S;
2 用钢成分(%):0.42C,0.29Si,0.69Mn,0.87Cr,0.14Ni,0.010P,0.013S。
表4-8-5 40Cr钢的热导率
温度/℃ | 100 | 200 | 300 | 400 | 500 | 600 |
热导率λ/W·(m·K)-1 | 32.6 | 30.9 | 29.3 | 28.0 | 26.7 | 25.5 |
热加工
40Cr钢的热加工工艺示于表4-8-6
表4-8-6 40Cr钢的热加工工艺
加热温度/℃ | 开始温度/℃ | 终止温度/℃ | 冷却方法/℃ |
<1200 | 1100~1150 | >800 | 大于60mm缓冷 |
40Cr钢材
的机械零件,如汽车的转向节、后半轴以及机床上的齿轮、轴、蜗杆、花键轴、顶尖套等;经淬火及中温回火后用于制造承受高负荷、冲击及中等速度工作的零件,如齿轮、主轴、油泵转子、滑块、套环等;经淬火及低温回火后用于制造承受重负荷、低冲击及具有耐磨性、截面上实体厚度在25mm以下的零件,如蜗杆、主轴、轴、套环等;经调质并高频表面淬火后用于制造具有高的表面硬度及耐磨性而无很大冲击的零件,如齿轮、套筒、轴、主轴、曲轴、心轴、销子、连杆、螺钉、螺帽、进气阀等。此外,这种钢又适于制造进行碳氮共渗处理的各种传动零件,如直径较大和低温韧性好的齿轮和轴。
弹性模
弹性模量E(20℃) /MPa 200000~211700 ,切变模量G(20℃) 80800
回火加热温度(℃):520;冷却剂:水、油
抗拉强度(σb/MPa):≥980
屈服点(σs/MPa):≥785
断后伸长率(δ5/%):≥9
断面收缩率(ψ/%):≥45
冲击吸收功(Aku2/J):≥47
布氏硬度(HBS100/3000)(退火或高温回火状态):≤207